[RTF] Reverse Treated ED Copper Foil

Short Description:

RTF, reverse treated electrolytic copper foil is a copper foil that has been roughened to varying degrees on both sides. This strengthens the peel strength of both sides of the copper foil, making it easier to use as an intermediate layer for bonding to other materials. Moreover, the different levels of treatment on both sides of the copper foil make it easier to etch the thinner side of the roughened layer. In the process of making a printed circuit board (PCB) panel, the treated side of the copper is applied to the dielectric material. The treated drum side is rougher than the other side, which constitutes a greater adhesion to the dielectric. This is the main advantage over standard electrolytic copper. The matte side does not require any mechanical or chemical treatment prior to the application of photoresist. It is already rough enough to have good laminating resist adhesion.

Send email to us Ask For Sample

Product Detail

Product Tags

Product Introduction

Specifications

CIVEN can supply RTF electrolytic copper foil with nominal thickness of 12 to 35µm up to 1295mm width.

Performance

The high temperature elongation reversed treated electrolytic copper foil is subjected to a precise plating process to control the size of the copper tumors and distribute them evenly. The reversed treated bright surface of the copper foil can significantly reduce the roughness of the copper foil pressed together and provide sufficient peel strength of the copper foil. (See Table 1)

Applications

Can be used for high-frequency products and inner laminates, such as 5G base stations and automotive radar and other equipment.

Advantages

Good bonding strength, direct multi-layer lamination, and good etching performance. It also reduces the potential for short circuit and shortens the process cycle time.

Table 1. Performance

Classification		Unit	1/3OZ (12μm)	1/2OZ (18μm)	1OZ (35μm)
Cu Content		%	min. 99.8
Area Weigth		g/m²	107±3	153±5	283±5
Tensile Strength	R.T.(25℃)	Kg/mm²	min. 28.0
	H.T.(180℃)		min. 15.0	min. 15.0	min. 18.0
Elongation	R.T.(25℃)	%	min. 5.0	min. 6.0	min. 8.0
	H.T.(180℃)		min. 6.0
Roughness	Shiny(Ra)	μm	max. 0.6/4.0	max. 0.7/5.0	max. 0.8/6.0
	Matte(Rz)		max. 0.6/4.0	max. 0.7/5.0	max. 0.8/6.0
Peel Strength	R.T.(23℃)	Kg/cm	min. 1.1	min. 1.2	min. 1.5
Degraded rate of HCΦ(18%-1hr/25℃)		%	max. 5.0
Change of color(E-1.0hr/190℃)		%	None
Solder Floating 290℃		Sec.	max. 20
Pinhole		EA	Zero
Preperg		----	FR-4