Product Introduction
Electrolytic copper foil for lithium batteries is a copper foil developed and produced by CIVEN METAL specifically for the lithium battery manufacturing industry. This electrolytic copper foil has the advantages of high purity, low impurities, good surface finish, flat surface, uniform tension, and easy coating. With higher purity and better hydrophilic, the electrolytic copper foil for batteries can effectively increase the charge and discharge times and extend the cycle life of batteries. At the same time, CIVEN METAL can slit according to customer’s requirements to meet customer’s material needs for different battery products.
Specifications
CIVEN can provide double-sided optical lithium copper foil in different widths from 4.5 to 20µm nominal thickness.
Performance
The products have the characteristics of symmetrical double-sided structure, metal density close to the theoretical density of copper, very low surface profile, high elongation and tensile strength (see Table 1).
Applications
It can be used as anode carrier and collector for lithium-ion batteries.
Advantages
Compared with single-sided gross and double-sided gross lithium copper foil, its contact area increases exponentially when it is bonded with the negative electrode material, which can significantly reduce the contact resistance between the negative electrode collector and the negative electrode material and improve the symmetry of the negative electrode sheet structure of lithium-ion batteries. Meanwhile, the double-sided light lithium copper foil has good resistance to cold and heat expansion, and the negative electrode sheet is not easy to break during the charging and discharging process of the battery, which can prolong the service life of the battery.
Table1. Performance
|
Test Item |
Unit |
Specification |
||||||
|
6μm |
7μm |
8μm |
9/10μm |
12μm |
15μm |
20μm |
||
|
Cu Content |
% |
≥99.9 |
||||||
|
Area Weight |
mg/10cm2 |
54±1 |
63±1.25 |
72±1.5 |
89±1.8 |
107±2.2 |
133±2.8 |
178±3.6 |
|
Tensile Strength(25℃) |
Kg/mm2 |
28~35 |
||||||
|
Elongation(25℃) |
% |
5~10 |
5~15 |
10~20 |
||||
|
Roughness(S-Side) |
μm(Ra) |
0.1~0.4 |
||||||
|
Roughness(M-Side) |
μm(Rz) |
0.8~2.0 |
0.6~2.0 |
|||||
|
Width Tolerance |
Mm |
-0/+2 |
||||||
|
Length Tolerance |
m |
-0/+10 |
||||||
|
Pinhole |
Pcs |
None |
||||||
|
Change of Color |
130℃/10min 150℃/10min |
None |
||||||
|
Wave or Wrinkle |
—- |
Width≤40mm one allow |
Width≤30mm one allow |
|||||
|
Appearance |
—- |
No drape, scratch, pollution, oxidation, discoloration and so on that effect using |
||||||
|
Winding method |
—- |
The winding when facing up S sideWhen the winding tension in the stable, no loose roll phenomenon. | ||||||
Note: 1. Copper foil oxidation resistance performance and surface density index can be negotiated.
2. The performance index is subject to our testing method.
3. The quality guarantee period is 90 days from the date of receipt.
Product detail pictures:
Related Product Guide:
Our rewards are lower costs,dynamic profits team,specialised QC,potent factories,high-quality services for OEM China Copper Nickel Alloy Foil - ED Copper Foils for Li-ion Battery (Double-shiny) – CIVEN , The product will supply to all over the world, such as: Albania, kazan, venezuela, We follow up the career and aspiration of our elder generation, and we are eager to open up a new prospect in this field, We insist on "Integrity, Profession, Win-win Cooperation", because we have a strong backup, that are excellent partners with advanced manufacturing lines, abundant technical strength, standard inspection system and good production capacity.
By Anna from Germany - 2018.12.25 12:43
This supplier's raw material quality is stable and reliable, has always been in accordance with the requirements of our company to provide the goods that quality meet our requirements.
By Zoe from Chile - 2018.09.29 17:23