Manufacturer for Brass Strips - RTF ED Copper Foil – CIVEN
Manufacturer for Brass Strips - RTF ED Copper Foil – CIVEN Detail:
Product Introduction
Reverse treated electrolytic copper foil (RTF) is a copper foil that has been roughened to varying degrees on both sides. This strengthens the peel strength of both sides of the copper foil, making it easier to use as an intermediate layer for bonding to other materials. Moreover, the different levels of treatment on both sides of the copper foil make it easier to etch the thinner side of the roughened layer. In the process of making a printed circuit board (PCB) panel, the treated side of the copper is applied to the dielectric material. The treated drum side is rougher than the other side, which constitutes a greater adhesion to the dielectric. This is the main advantage over standard electrolytic copper. The matte side does not require any mechanical or chemical treatment prior to the application of photoresist. It is already rough enough to have good laminating resist adhesion.
Specifications
CIVEN can supply RTF electrolytic copper foil with nominal thickness of 12 to 35µm up to 1295mm width.
Performance
The high temperature elongation reversed treated electrolytic copper foil is subjected to a precise plating process to control the size of the copper tumors and distribute them evenly. The reversed treated bright surface of the copper foil can significantly reduce the roughness of the copper foil pressed together and provide sufficient peel strength of the copper foil. (See Table 1)
Applications
Can be used for high-frequency products and inner laminates, such as 5G base stations and automotive radar and other equipment.
Advantages
Good bonding strength, direct multi-layer lamination, and good etching performance. It also reduces the potential for short circuit and shortens the process cycle time.
Table 1. Performance
|
Classification |
Unit |
1/3OZ (12μm) |
1/2OZ (18μm) |
1OZ (35μm) |
|
|
Cu Content |
% |
min. 99.8 |
|||
|
Area Weigth |
g/m2 |
107±3 |
153±5 |
283±5 |
|
|
Tensile Strength |
R.T.(25℃) |
Kg/mm2 |
min. 28.0 |
||
|
H.T.(180℃) |
min. 15.0 |
min. 15.0 |
min. 18.0 |
||
|
Elongation |
R.T.(25℃) |
% |
min. 5.0 |
min. 6.0 |
min. 8.0 |
|
H.T.(180℃) |
min. 6.0 |
||||
|
Roughness |
Shiny(Ra) |
μm |
max. 0.6/4.0 |
max. 0.7/5.0 |
max. 0.8/6.0 |
|
Matte(Rz) |
max. 0.6/4.0 |
max. 0.7/5.0 |
max. 0.8/6.0 |
||
|
Peel Strength |
R.T.(23℃) |
Kg/cm |
min. 1.1 |
min. 1.2 |
min. 1.5 |
|
Degraded rate of HCΦ(18%-1hr/25℃) |
% |
max. 5.0 |
|||
|
Change of color(E-1.0hr/190℃) |
% |
None |
|||
|
Solder Floating 290℃ |
Sec. |
max. 20 |
|||
|
Pinhole |
EA |
Zero |
|||
|
Preperg |
—- |
FR-4 |
|||
Note: 1. The Rz value of copper foil gross surface is the test stable value, not a guaranteed value.
2. Peel strength is the standard FR-4 board test value (5 sheets of 7628PP).
3. Quality assurance period is 90 days from the date of receipt.
Product detail pictures:
Related Product Guide:
To be able to ideal satisfy client's requirements, all of our operations are strictly performed in line with our motto "High High-quality, Competitive Price tag, Fast Service" for Manufacturer for Brass Strips - RTF ED Copper Foil – CIVEN , The product will supply to all over the world, such as: Roman, European, Egypt, We've got constructed strong and long co-operation relationship with an enormous quantity of companies within this business in Kenya and overseas. Immediate and professional after-sale service supplied by our consultant group has happy our buyers. Thorough Info and parameters from the merchandise will probably be sent for you for any thorough acknowledge. Free samples may be delivered and company check out to our corporation. n Kenya for negotiation is constantly welcome. Hope to get inquiries type you and construct a long-term co-operation partnership.