Brass Sheet
Product Introduction
Brass Sheet based on electrolytic copper, zinc and trace elements as its raw material, through processing by ingot, hot rolling, cold rolling, heat treatment, surface cleaning, cutting, finishing, and then packing. Material processes performance, plasticity, mechanical properties, corrosion resistance, performance and good tin. It has been widely used in electrical, automotive, communications, hardware, decoration and other industries
Main Technical Parameters
2-1Chemical Composition
|
Name |
Alloy No. |
Chemical Composition (%, Max.) |
||||||||
|
Cu |
Fe |
Pb |
Al |
Mn |
Sn |
Ni |
Zn |
Impurity |
||
|
Brass |
H96 |
95.0-97.0 |
0.10 |
0.03 |
--- |
--- |
--- |
0.5 |
Rem |
0.3 |
|
H90 |
88.0-91.0 |
0.10 |
0.03 |
--- |
--- |
--- |
0.5 |
Rem |
0.3 |
|
|
H85 |
84.0-86.0 |
0.10 |
0.03 |
--- |
--- |
--- |
0.5 |
Rem |
0.3 |
|
|
H70 |
68.5-71.5 |
0.10 |
0.03 |
--- |
--- |
--- |
0.5 |
Rem |
0.3 |
|
|
H68 |
67.0-70.0 |
0.10 |
0.03 |
--- |
--- |
--- |
0.5 |
Rem |
0.3 |
|
|
H65 |
63.5-68.0 |
0.10 |
0.03 |
--- |
--- |
--- |
0.5 |
Rem |
0.3 |
|
|
H63 |
62.0-65.0 |
0.15 |
0.08 |
--- |
--- |
--- |
0.5 |
Rem |
0.5 |
|
|
H62 |
60.5-63.5 |
0.15 |
0.08 |
--- |
--- |
--- |
0.5 |
Rem |
0.5 |
|
2-2 Alloy Table
|
Name |
China |
ISO |
ASTM |
JIS |
|
Brass |
H96 |
CuZn5 |
C21000 |
C2100 |
|
H90 |
CuZn10 |
C22000 |
C2200 |
|
|
H85 |
CuZn15 |
C23000 |
C2300 |
|
|
H70 |
CuZn30 |
C26000 |
C2600 |
|
|
H68 |
--- |
--- |
--- |
|
|
H65 |
CuZn35 |
C27000 |
C2700 |
|
|
H63 |
CuZn37 |
C27200 |
C2720 |
|
|
H62 |
CuZn40 |
C28000 |
C2800 |
2-3 Features
2-3-1 Specification Unit:mm
|
Name |
Alloy No.(China) |
Temper |
Size(mm) |
||
|
Thickness |
Width |
Length |
|||
|
Brass |
H59 H62 H63 H65 H68 H70 |
R |
4～8 |
600～1000 |
≤3000 |
|
H62 H65 H68 |
Y Y2 |
0.2～0.49 |
600 |
1000～2000 |
|
|
0.5～3.0 |
600～1000 |
1000～3000 |
|||
Temper Mark:O. Soft;1/4H. 1/4 Hard;1/2H. 1/2 Hard;H. Hard;EH. Ultrahard;R. Hot Rolled.
2-3-2 Tolerance Unit: mm
|
Thickness |
Width |
|||||
|
Thickness Allow Deviation ± |
Width Allow Deviation ± |
|||||
|
＜400 |
＜600 |
＜1000 |
＜400 |
＜600 |
＜1000 |
|
|
0.5~0.8 |
0.035 |
0.050 |
0.080 |
0.3 |
0.3 |
1.5 |
|
0.8~1.2 |
0.040 |
0.060 |
0.090 |
0.3 |
0.5 |
1.5 |
|
1.2~2.0 |
0.050 |
0.080 |
0.100 |
0.3 |
0.5 |
2.5 |
|
2.0~3.2 |
0.060 |
0.100 |
0.120 |
0.5 |
0.5 |
2.5 |
|
Temper |
Tensile Strength N/mm2 |
Elongation ≥% |
Hardness HV |
|
|
M |
(O) |
≥290 |
35 |
--- |
|
Y4 |
(1/4H) |
325-410 |
30 |
75-125 |
|
Y2 |
(1/2H) |
340-470 |
20 |
85-145 |
|
Y |
(H) |
390-630 |
10 |
105-175 |
|
T |
(EH) |
≥490 |
2.5 |
≥145 |
|
R |
--- |
--- |
--- |
|
Temper Mark:M. Soft;Y4. 1/4 Hard;Y2. Hard;Y. Hard;T. Ultra hard.
Manufacturing Technique