[BCF] Battery ED Copper Foil

Short Description:

BCF, battery copper foil for batteries is a copper foil developed and produced by CIVEN METAL specifically for the lithium battery manufacturing industry. This electrolytic copper foil has the advantages of high purity, low impurities, good surface finish, flat surface, uniform tension, and easy coating. With higher purity and better hydrophilic, the electrolytic copper foil for batteries can effectively increase the charge and discharge times and extend the cycle life of batteries. At the same time, CIVEN METAL can slit according to customer’s requirements to meet customer’s material needs for different battery products.

Send email to us Ask For Sample

Product Detail

Product Tags

Product Introduction

BCF, battery copper foil for batteries is a copper foil developed and produced by CIVEN METAL specifically for the lithium battery manufacturing industry. This electrolytic copper foil has the advantages of high purity, low impurities, good surface finish, flat surface, uniform tension, and easy coating. With higher purity and better hydrophilic, the electrolytic copper foil for batteries can effectively increase the charge and discharge times and extend the cycle life of batteries. At the same time, CIVEN METAL can slit according to customer's requirements to meet customer's material needs for different battery products.

Specifications

CIVEN can provide double-sided optical lithium copper foil in different widths from 4.5 to 20µm nominal thickness.

Performance

The products have the characteristics of symmetrical double-sided structure, metal density close to the theoretical density of copper, very low surface profile, high elongation and tensile strength (see Table 1).

Applications

It can be used as anode carrier and collector for lithium-ion batteries.

Advantages

Compared with single-sided gross and double-sided gross lithium copper foil, its contact area increases exponentially when it is bonded with the negative electrode material, which can significantly reduce the contact resistance between the negative electrode collector and the negative electrode material and improve the symmetry of the negative electrode sheet structure of lithium-ion batteries. Meanwhile, the double-sided light lithium copper foil has good resistance to cold and heat expansion, and the negative electrode sheet is not easy to break during the charging and discharging process of the battery, which can prolong the service life of the battery.

Table 1: Performance(GB/T5230-2000、IPC-4562-2000)

Test Item	Unit	Specification
Test Item	Unit	6μm	7μm	8μm	9/10μm	12μm	15μm	20μm
Cu Content	%	≥99.9
Area Weight	mg/10cm²	54±1	63±1.25	72±1.5	89±1.8	107±2.2	133±2.8	178±3.6
Tensile Strength(25℃)	Kg/mm²	28~35
Elongation(25℃)	%	5~10			5~15			10~20
Roughness(S-Side)	μm(Ra)	0.1~0.4
Roughness(M-Side)	μm(Rz)	0.8~2.0						0.6~2.0
Width Tolerance	Mm	-0/+2
Length Tolerance	m	-0/+10
Pinhole	Pcs	None
Change of Color	130℃/10min 150℃/10min	None
Wave or Wrinkle	----	Width≤40mm one allow						Width≤30mm one allow
Appearance	----	No drape, scratch, pollution, oxidation, discoloration and so on that effect using
Winding method	----	The winding when facing up S sideWhen the winding tension in the stable, no loose roll phenomenon.